LC Steel Shot

Chemical Form:%C; 0.10-0.15,
%Mn; 1.20-1.50, %Si; 0.10-0.25,
%S; 0.035 Max, %P; 0.035 Max.
Hardnsess: 40-50 HRC (Surface Finishing)
Micro Form: Bainitic

HC Steel Shot

Chemical Form: %C; 0.85-1.20, %Si; 0.4 Min,
%S; 0.05 Max, %P; 0.05
Hardness: 40-50 HRC (Surface Finishing),
45-52 HRC (Shot Peening)
Micro Form: Martensite

Steel Shot

Asal Metal 2007 ã All rights reserved
Fast
Access
Site Map
Shot Blasting Machines  |  Stainless Steel Shot  |  Glass Beads  |  Aluminium Oxide  |  Cut Wire  |  Blasting Cabinets  |  Blasting Media  |  Vibratory Finishing Machines  |  Vibratory Finishing Media  |  Hook Type Shot Blasting Machine  | Contract Job Shot Blasting  |  Shot Peening Media  |  Steel Shot  |  Contract Job Vibratory  |  Steel Grit  |  Stainless Steel Grit |  Conditioned Cut Wire  |  Air Blasting Machine
Foundry Chemicals and Foundry Products
Shot Blasting Machines and Blasting Media - Vibratory Finishing Machines and Media
SAE NO


S 70




S 110




S 170




S 230




S 280




S 330




S 390




S 460




S 550




S 660




S 780
Nominal Diameter (mm)


0,20 mm




0,30 mm




0,42 mm




0,60 mm




0,71 mm




0,84 mm




1,00 mm




1,19 mm




1,41 mm




1,68 mm

S 230




S 280




S 330




S 390




S 460




S 550




S 660




S 780
S 330




S 390




S 460




S 550



S 660




S 780
0,71 mm




0,84 mm




1,00 mm




1,19 mm




0,60 - 1,00 mm




0,70 - 1,25 mm




1,00 - 1,40 mm




1,25 - 1,70 mm




1,04 - 2,00 mm




1,70 - 3,00 mm

1,41 mm


1,68 mm


2,00 mm


Sieve Range (mm)


0,125 - 0,355




0,180 - 0,500




0,355 - 0,710




0,500 - 0,850




0,71 mm




0,84 mm




1,00 mm




1,19 mm




1,41 mm




1,68 mm

0,600 - 1,00




0,710 - 1,18




0,850 - 1,40




1,00 - 1,70




1,18 - 2,00




0,70 - 1,25 mm




1,00 - 1,40 mm




1,25 - 1,70 mm




1,04 - 2,00 mm




1,70 - 3,00 mm

1,18 - 2,00


1,40 - 2,36


1,70 - 2,80


S 280




S 330




S 390




S 460




S 550




S 660




S 780
gallery+blasting
Density:
7,3g/cm3

Steel shot refers to spherical grains made of molten steel through an atomization ("granulation") process, available in different sizes and hardnesses.